A modified ion-plated TiN(IP-TiN) coating has been developed by adding 6 wt-% A1 and small amounts of La.Examination of this coating showed that the adhesion between the coat- ing and substrate is remarkably improved by the La added up to 2 wt-% ,and the microhardness and wear resistance of the coating surface closely relate to the contents of La.EPMA and X-ray diffraction analysis indicated that a thick transition zone forms owing to the addition of La and A1.The phase composition and grain orientation of the coating change because of the formation of such transition zone.Thus,the properties of coating were improved.
关键词:
ion plated TiN coating
,
null
,
null
,
null
LI Ruiguo FENG Jun FENG Zhongchao Corrosion Science Laboratory.Institute of Corrosion and Protection of Metals. Academia Sinica
,
Shenyang
,
110015
,
ChinaInstitute of Metal Research
,
Academia Sinica.Shenyang 110015
,
China
材料科学技术（英）
Silicon was added to the surface of 304 stain- less steel by laser melting the sprayed preplaced Si powders.The optical microscopy,X-ray diffraction and EPMA were employed to investigate the microstructure and chemical composition of the laser surface alloyed layer.The hardness of the al- loyed layer was measured by microhardness test and wear resistance was evaluated by scratch test. Corrosion resistance of laser alloyed sample was studied in 1N H_2SO_4+0.1N NaCl and 0.5N HCl+0.5N NaCl aqueous solutions.A microcrystalline intermetallic compound coating with smooth surface and good chemical homogeneity without porosity and crack is ob- tained.The hardness is about 720 HV.The wear re- sistance is 2 times better than that of the substrate. The corrosion resistance of the laser alloyed sample is much better than that of 304 stainless steel sample.